The composite SiO$_2$/Si$_3$N$_4$/SiO$_2$(ONO) film formed by oxidation on nitride film has been widely studied as DRAM stacked capacitor multi-dielectric films. Load lock(L/L) LPCVD system by HF cleaning is used to improve electrical capacitance and to scale down of effective thickness for memory device, but is brings a new problem. Nitride film deposited using HF cleaning shows selective deposition on poly silicon and oxide regions of capacitor. This problem is avoidable by carpeting chemical oxide using $H_2O$$_2$cleaning before nitride deposition. In this paper, we study the limit of nitride thickness for abnormal oxidation and the initial deposition time for nitride deposition dependent on underlayer materials. We proposed an advanced fabrication process for stacked capacitor in order to avoid selective deposition problem and show the usefulness of nitride deposition using L/L LPCVD system by $H_2O$$_2$cleaning. The natural oxide thickness on polysilicon monitor after HF and $H_2O$$_2$cleaning are measured 3~4$AA$, respectively. Two substrate materials have the different initial nitride deposition times. The initial deposition time for polysilicon is nearly zero, but initial deposition time for oxide is about 60seconds. However the deposition rate is constant after initial deposition time. The limit of nitride thickness for abnormal oxidation under the HF and $H_2O$$_2$cleaning method are 60$AA$, 48$AA$, respectively. The results obtained in this study are useful for developing ultra thin nitride fabrication of ONO scaling and for avoiding abnormal oxidation in stacked capacitor application.