In this paper, we fabricated $SnO_2$ composite ceramics doped with 0~20mol% $SnO_2$ of bulk type to investigate the CO and $H_2$ gas sensitivity in various composition, temperature, and concentration of CO and $H_2$ gas. At the temperature range from $100^{circ}Csim425^{circ}C$, the measured 1000ppm and 250ppm CO gas sensitivities of $SiO_2-SnO_2$composite ceramics were about 1.0~7.6 and 1.0~5.6, respectively. These values were about 1.0~1.5 times larger than pure $SnO_2$. The maximum 1000ppm CO gas sensitivity of $SiO_2-SnO_2$composites were measured around $325^{circ}C$. At the temperature range from $270^{circ}Csim380^{circ}C$, the 1000ppm and 500ppm $H_2$gas sensitivities of $SiO_2-SnO_2$ composites were about 2.9~21.2 and 2.1~11.3, respectively. Also the maximum 1000, 500 ppm $H_2$ gas sensitivities of samples were measured around.