CoPtCr magnetic layer was fabricated on the Cr underlayer by RF magnetron sputtering and the protective $SiO_2$ layer was deposited at room temperature. As the thickness of Cr underlayer increased, the coercive force of magnetic layer increased, then saturated slightly further increasing Cr underlayer thickness. Maximum coercive force was 860 Oe. It is thought that in-plane arrangement of magnetic phase and magnetic decoupling between the magnetic crystallites could lead to the increase of the coercive force. Post-annealing raised the coercive force exceedingly. and maximum coercive force value was 1650 Oe which was acquired from the sample annealed at 55$0^{circ}C$ for 1hr.