The electrical conductivity of undoped mtile was measured in the oxygen partial pressure range of $1~10{-23}$atm and temperature range of $700~1300^{circ}C$ to investigate the defect types and the electrical properties. The data(logu/logPoz) were divided into the five regions. Therefore the five dominant defect types such as $Ti_nO_{2n-1}$, Ti, Vo, Vo due to impurity, and n-p transition or p-type conduction with the Poz and the temperature were proposed. The formation enthalpies calculated from these experimental results were found to be 10.2eV for Ti, and 4. 92eV for Vo in intrinsic range.