The solid-phase crystallization (SPC) of plasma-enhanced chemical vapor depsoited (PECVD) amorphous silicon (a-Si) films ha s been investigated by x-ray diffraction (XRD). The a-Si films were prepared on Si (100) wafers using $SiH_4$ gas and without $H_2$ dilution at the substrate temperatures between $120^{circ}C$ and $380^{circ}C$, and than annealed at $600^{circ}C$ for crystallization. The annealed samples exhibited (111), (220), and (311) XRD peaks with preferential orientation of (111). The XRD peak intensities increased as the substrate temperature decreased, and the $H_2$dilution suppressed the solid-phase crystallization. The average grain size estimated by XRD analysis for the (111) texture has increased from about 10 nm to about 30 nm, as the substrate temperature decreased. The deposition rate also increased with the decreasing substrate temperature and the grain size was closely dependent on the deposition rate of the films. The grain size enhancement was attributed to an increase of the structural disorder of the Si network.