It is necessary to use Arc layer and DUV resist to define 0.25 $mu extrm{m}$ line and space for 256 MDRAM devices. Poly-Si etching with Arc layer and different resists has been performed in a TCP-9408 etcher with variation of gas chemistries; $Cl_2/O_2, Cl_2/N_2, Cl_2$/HBr . DUV resist causes more positive etch profile and CD gain compared to I-line resist because the sidewall passivation is more stimulated by increasing polymerization through the loss of resist. When Arc layer is applied, CD hain also increases due to the polymeric mask formed after thching Arc layer. From the point of gas chemistry effects, the etch profile and CD gain is not improved using $Cl_2/O_2$ gas, since polymerization is accelerated in this gas. however, the vertical profile and less CD gain is obtained using $Cl_2$/HBr gas. Furthermore, HBr gas is very effective to suppress the difference of profile and CD variation between dense pattern and isolated pattern by minimizing non-uniformity of side wall passivation with pattern density.