As device dimensions approach submicrometer size in ULSI, the demand for interlayer dielectric materials with very low dielectric constant is increased to solve problems of RC delay caused by increase in parasitic resistance and capacitance in multilevel interconnectins. Fluorinated amorphous carbon in one of the promising materials in ULSI for the interlayer dielectric films with low dielectric constant. However, poor thermal stability and adhesion with Si substrates have inhibited its use. Recently, amorphous hydrogenated carbon (a-C:H) film as a buffer layer between the Si substrate and a-C:F has been introduced because it improves the adhesion with Si substrate. In this study, therfore, a-C:F/a-C:H films were deposited on p-type Si(100) by ECRCVD from $C_2F_6, CH_4$and $H_2$gas source and investigated the effect of forward power and composition on the thickness, chemical bonding state, dielectric constant, surface morphology and roughness of a-C:F films as an interlayer dielectric for ULSI. SEM, FT-IR, XPS, C-V meter and AFM were used for determination of each properties. The dielectric constant in the a-C:F/a-C:H films were found to decrease with increasing fluorine content. However, the dielectric constant increased after furnace annealing in $N_2$atomosphere at $400^{circ}C$ for 1hour due to decreasing of flurorine content. However, the dielectric constant increased after furnace annealing in $N_2$atmosphere at $400^{circ}C$ for 1hour due to decreasing of fluorine concentration.