The composition and the properred orientation of Co-Fe-Cr alloy electrodeposits were invesigated according to the electrolysis conditions using sulface bath. The current efficiency and the cathode overpotential decrased noticeably with the increase of Cr content in the bath. As the D.C. current density increased increased, the Cr content in the alloy increasd, while Co content decreased and Fe content remained constant, In the pulse current electrolysis, the Cr content of the alloy increased with the mean current density and off-time and then its content increased mord more noticeably with the peak current density than that of D.C. electrolysis. The preferred orientation of the alloy changed from (220)+(111) to (220) with decreasing cathode overpotential.