The microwave dielectric properties of X BaO-0.15($Nd_{0.87}Bi_{0.13})_2O_3-(0.85-X)TiO_2 (X=0.14~0.17) and 0.16BaO-0.15(Bi_xNd_{1-x})_2O_3-0.69TiO_2$ (X=0.12~0.15) ceramics sintered at 1320~$1380^{circ}C$ were investigated. The microwave dielectric properties of X BaO-0.15(Nd_{0.87}Bi_{0.13})_2O_3-(0.85-X)TiO_2$</TEX> (X=0.14~0.17) can be controlled effectively by adjusting X content : with increasing X from 0.14 to 0.17 both dielectric constant and temperature coefficient of resonant frequency decreased from 94.6 to 86 and from 22 ppm/^${circ}C to -7 ppm/^{circ}C$, respectively, while quality factor increased from 1300 to 1920 (at 4GHz). The microwave dielectric properties of 0.16BaO-0.15(Bi_x/Nd_{1-x2}O_3 -0.69TiO_2$</TEX> (X=0.12~0.15) can be controlled effectively by adjusting X content : with increasing X from 0.12 to 0.15 both quality factor and temperature coefficient of resonant frequency decreased from 1920 to 1430 and from 9 ppm/^${circ}C to -10 ppm/^{circ}C$, respectively, while dielectric constant increased from 87.5 to 92.6.