In order to lower porosity of the porous silica, titanium alkoxide solution was filled in the pore of silica in the heating-vacuum condition. The specific surface area of modified samples was decreased effectively from 900 m$^2$/g to 100 m$^2$/g. (The aggregation phenomena in modified samples were improved fairly.) Samples were heated at 600 , and then the titanium alkoxide in the pore was decomposed completely to titanium oxide from TGA-DTA measurement. From SEM result, it was evident that titanium oxide did not coat the surface of the silica. The modified samples were analyzed using SEM, DTA-TGA, BET, and UV-visible spectrometer.