This study was to investigate the effect of .compressive load and cyclic humidity(2$0^{circ}C$, 65% and 90% RH) on the physical and mechanical properties of corrugated board. Corrugated boards in the study were under compressive load and under cyclic humidity, and their properties were compared to those without load. Results were summarized as follows ; 1 Statistically significant correlation was shown between the ring crush of the boards and the compressive strength of cylinder specimen made from the boards. So we could study the compressive behavior of board with cylinder specimen. 2. The boards under the compressive load increased their moisture content and thickness much more than those without load both in constant and in cyclic RH. 3. The compressive and tensile strength of board samples were inversely and closely proportional to the sheet moisture content regardless of their load and humidity history. 4. The moisture content did not show any significant proportionality to the change of burst strength of boards within this experiment. 5. Board reconditioning in standard condition led to the recovery of the strength loss that had occurred under various load and humidity condition. 6. The handsheets prepared from the boards that had experienced compressive load and cyclic humidity, and those with no-load and 65% RH did not show any significant difference in strength properties. No physical damage or load-carrying properties of the wood fiber were observed by the compressive load and cyclic humidity history.