The effects of alloying elements(Mo, Cu, Ni) and austempering temperature conditions on the microstructural morphologies and mechanical properties in austempered ductile cast iron has been investigated. The austempering at $350^{circ}C$ for 2hrs after austenitizing at $900^{circ}C$ for 2hrs in all specimens with various alloying elements was optimum because the good combination of tensile and yield strength, hardness and impact value was obtained. The microstructures of these ADIs treated by a forementioned austempering condition are nearly a mixture type of needle and feathery bainite. Among those alloys, Mo-Cu alloyed DCI had the best optimum mechanical properties of hardness and toughness for automobile parts by austempering treatment for 2hrs at $900^{circ}C$ followed by $350^{circ}C$ for 2hrs.