This paper presents an investigation why Mn-steel high pressure gas cylinders have been failed in service. The fractured cylinders have been collected to identify the reason of the failure using various methods. The undamaged, new cylinder has also been tested for the base data. We examined the chemical compositions and fracture facets as well as the mechanical properties of the vessels. The microstructural observations of the fractured regions of the cylinder did not indicate the noticeable defects which might cause the failure. The experiments of cylinders on the compositinal and mechanical tests showed that the cylinder was in good shape according the standards of gas pressure vessel. The morphological analysis of the fracture surfaces concluded that the origin of the failure was the local weak segments induced by the external impact to the cylinder, which result in a sudden, fast fracture.