Many dental composites are Bis-GMA based resin which diluted with the more fluid monomer triethylenglycol dimethacrylate(TEGDMA). TEGDMA is often present in exess so that some quantity remains unreacted following photo-initiated polymerization. TEGDMA is a component of some resin composites which contributes to their cytotoxicity. The presence of dentin between resin composite and pulp space reduce the cytotoxicity in vitro. The root system from extrcted human third molar was removed and then a circular occlusal cavity 4mm in diameter was prepared, leaving a remaining dentinal thickness to the roof of the pulpal chamber within the range 1.0-1.5mm. Dentine was treated with 37% phosphoric acid prior to Z 100 placement without using bonding resin(group 1). In group 2, SMP(Scotchbond Multi Purpose) primer, bonding resin prior to Z 100 placement were applied sequently. In group 3, moulds with internal dimensions 4mm diameter by 2mm depth were used to contain the composite alone with an equvalent mass on tooth model, and then they were immersed directly into water. The purpose of this study is to evaluate the release rate and quantity of TEGDMA with or without the application of bonding resin. Both release rate and total cumulative amount of TEGDMA for the three groups were determined using reversed-phase HPLC at times up to 10 days. The results were as follows: 1. All experimental groups showed the highest rate of release was in the first sample period(0-4.32 min) and the rate of release declined exponentially thereafter. 2. The maximum release rate and total cumulative account of TEGDMA in the tooth model of group 1 and group 2 with the use of SMP bonding resin were reduced however ther were no significant differences between these groups(P>0.05). 3. In the first sample period(0-4.32 min), the rate of release of TEGDMA from composite resin in group 3 immersed directly into water was significantly higher than that in group 1 and group 2 of tooth model(P<0.05). Conclusively, TEGDMA diffusion from Z 100 resin was not effectively prevented by the presence of dentin in spite of using the SMP bonding resin.