The repassivation characteristics of Fe-Cr steels in deaerated 0.1 M $Na_2SO_4$ solution have been investigated with the variation of Cr content, applied potential and Cl- concentration. In the absence of chloride ion, abrading electrode test showed that, slope -n, of log i=k -n log t, a parameter of repassivation rate, approached to -1, regardless of Cr content but as Cr content increased, repassivation current density decreases with increasing Cr content. A.C. Impedance spectroscopy showed that the charge transfer resistance of passive film became higher as Cr content and applied potential increased. However, in the presence of chloride ion, it was observed that chloride ion suppressed the passive film formation, whose effect became greater with increasing applied potential.