The influence of ambient gases on field emission performance of Mo-field emitter array(FEA) in the frit-sealing step of field emission display(FED) packaging process was investigated. Mo-tip FEA was mounted on the glass substrate having a surrounded frit(Ferro FX11-137) and fired at $415^{circ}C$ in the ambient gases of air, $N_2$ and Ar. The Ar gas was proved to be most proper ambient among the used gases through evaluating the turn-on voltage and field emission current of the fired Mo-tip FEA devices. It was confirmed that the Mo surface fired in Ar ambient was less oxidized when compared with another ones annealed in air and Ar ambient by the AFM, XPS, AES and SIMS analysis. Finally, the 3.5 inch-sized Mo-tip FED, which was packaged using frit-sealing process in the Ar ambient, was proposed.