This paper was carried out to know the influence of advanced austempered ductile cast iron (ADI) on the tool life and mechanical properties of drilling machinability. For manufactured method of ADI, the spheroidal graphite cast iron were austenized at 90$0^{circ}C$ for 1 hour and then austempered for 2 hour at 37$0^{circ}C$ in the salt bath. And interrelationship has been investigated between tool life and mechanical characteristics of specimen material on drilling condition when the ordinary and step-feed drilling are carried out to drill holes of specimens. Tensile strength and hardness of ADI decrease and elongation of ADI increases with the increase austempered temperature. It is known that about 2 times of tool life in the case of step-feed decreases compared with ordinary feed due to the high hardness of ADI and hardness ascribed to the fact that retained austenite became to martensite state due to cutting heat in drilling. Under the constant feed rate 0.1mm/rev relation between hardness and length of end tip after drilling can be formularized to Hv=$788.46L^{-0.096}$ for the cutting speed 6.1m/min.