$Cd_{1-x}Mn_xTe$ thin films were grown on GaTs (100) substrates by hot-wall epitaxy method. From the XRD measurements, it was found that CdTe/GaAs (100)film was grown as a single crystal with the same growth plane of (100) and $Cd_{1-x}Mn_xTe$film as a poly crystal as Mn content was increased, and the lattice constant was decressed with the similar gradient of bulk crystal as x was increased. From the PL measurements, $L_1$line due to the exciton trapped on an acceptor and $L_2$line due to an exciton trapped on a shallow potential fluctuation were observed, and $L_1$line was observed only in $Cd_{0.91}Mn_{0.09}$te but it was disappeared probably due to a stronger lacalization of excitons with increasing alloy fluctuation.$L_2$line was dominant in case of $x{ge}0.2$and for higher Mn contents the broad transition about 2.0eV associated to the 3d levels of the $Mn^{2+}$ ion dominated the PL spectrum, and the $L_2$ transition become weaker and weaker. For$x{ge}0.4$, the transition line about 2.0eV due to $Mn^{2+}$ion showed no shift.