Three mixtures of elemental powders of Al-25at.%Ti, 48at.%Ti and 70at.%Ti were offered to ball milling process for the formation of intermetallic compounds of $Al_3Ti$, AlTi and $Ti_3Al$. Ballmilling or attrition process were carried out at the condition of rotaing speed of 110 or 350 rpm at $10^{-3}$ torr vacuum or argon atmospheres. $Al_3Ti$phases were fully obtained by heat treatment for 1 hors at $600^{circ}C$ with Al-25at.%Ti composition mixtures milled by 100 hours. The amorphous phase was completely formed at the composition of Al-48at.%Ti mixed powders by milling 100hours at the 50 to 1 weight ratio of ball to powder, and AlTi compounds were obtained by heat treament. In the case of Al-70at%Ti mixed powders milled for 100 hours, $Ti_3Al$ and $Al_3Ti$intermetallic compounds were formed by heat treatment for 1 hour at $600^{circ}C$. By attrition milling of 350rpm for 10 hours, $Ti_3Al$ phase was formed completley after heat treatment for 1 hour at $600^{circ}C$.