The dielectric and pyroelectric properties of $Ba_{0.66}$$Sr_{0.38}$$TiO_{3}$(BST) thin films growtn on Pt/Ti/NON/Si us-ing RF magnetron sputtering have been investigated. With increasing the substrate temperature during de-position of the BST film in the range of 300-$600^{circ}C$ the dielectric and pyroelectric constants of the film were increased due to improved crystallinity of the film. In addition the dependence of the microstructural and electrical properties of BST films onthe deposition temperature of the bottom Pt electrode was studied. The preferred orientation of the BST films as well as the microstructure of the Pt film was greatly in-fluenced by the deposition temperature of the bottom Pt electrode was studied. The preferred orientation of the BSt films as well as the microstructure of the Pt film was greatly in-fluenced by the deposition temperature of the bottom Pt electrodes. and thus so were the pyrolelectric pro-perties of the BST film. The highest value of pyroelectric coefficient at room temperature obtained in this work was $nCcm^{-2}K^{-1}$ which is much higher than those previously reported on other perovskite fer-roelectric thin films.