Ceramic tapes were fabricated by ultrasonically spraying slurries of monodispersed spherical and alumina powders. Effects of slurry compositions on tape forming were investigated. A relatively fast rate of solvent evaporation caused pores and cracks to be formed. A good chemical affinity between solvent and binder gave rise to binder separation resulting in inhomogeneous distribution of binder. Defect-free silica tapes with uniform distribution of particle packing and the binder were obtained from the solvent having a low chemical affinity and a slow evaporation rate and containing appropriate amounts of the binder and the plasticizer. Tape thickness could be controlled by adjusting solids loadings and slurry feed rates. It was possible to fabricate a tape in 15 $mu extrm{m}$ thickness from 7 vol% alumina slurry.