Porous alumina was fabricated from pressureless powder packing forming method using powders granulated by spray drying. It was investigated the pore size distribution of fabricated porous alumina. The results of microstructural observation showed that intraganular pore size and intragranular pore size. At 1700$^{circ}C$ there were no intragranular pores but it showed homogeneous distribution of intergranular pore size. The bending strength and shrinkage increased as porosity decreased. In case of thermal shock resistance sudden decrease of bending strength to $Delta$T was not shown because intergranular large pore prevented sudden crack propagation.