Sandwich structures of$ Nd_2Fe_{14}B/Fe/Nd_2Fe_{14}B $magnetic films have been grown by a KrF excimer laser (λ=248 nm) ablation technique. Magnetic properties were characterized by varying the thickness of hard ($Nd_2Fe_{14}B$) and soft (Fe) magnetic films and the volume fraction as well. In the (x)nm[NdFeB]/(y)nm[Fe]/(x)nm[NdFeB]/(100) Si structure the thickness (x) was varied from 3.6 to 54 nm, and (y) from 15 to 112 nm. At (y) = 15~20 nm where the volume fraction of Fe corresponded to 61~75%, the sandwich structure exhibited an enhanced Mr/Ms and iHc as well from the result of the exchange coupling between the magnetic layers. Experimentally calculated exchange constant$ (A_s) of A_s = 2.5{ imes}10^{-10} J/m$ was estimated using the intrinsic coercivity (iHc) of 1.2 kOe at 5 K for the sandwich magnetic trilayers.