The recovery activation energy, the order of reaction and the recovery rate constant were detemined by isochronal and isothermal annealing treatment to investigate the recovery behaviors of neutron irradiated Mn-Mo-Ni low alloy steels$(fluence: 2.3 imes10^{19}ncm^{-2}, 553K, Egeq1.0 MeV)$. Vickers microhardness tests were conducted to trace the recovery behavior after heat treatments. The results were analyzed in terms of recovery stages, behavior of responsible defects and recovery kinetics. It was shown that recovery occurred through two annealing stages(stage I : 703-753K, stage n : 813-873K) with re$infty$very activation energies of 2.5 eV and 2.93 eV for each stage I and n, respectively. From the comparison of unirradiated and irradiated isochronal anneal curves, a radiation anneal hardening(RAH) peak was identified at around 813K. Most of recovery have occurred during about 120 min irrespective of isothermal annealing temperatures of 743K and 833K. Recovery rate constants were determined to be $3.4 imes10^{-4}min^{-1} and 7.1 imes10^{-4}min^{-1}$ for stage I and II, respectively. The order of reaction was about 2 for both recovery stages. Comparing the obtained data with those of previously reported results on neutron irradiated Mn- Mo- Ni steels, the thermal recovery be­havior of the present material seems to occur by the dissociation of point defect clusters formed during irradiation, and by the recombination process of self-interstitials and vacancies from dissociated vacancy clusters.