The tensile strength and water resistance of ADC12 alloy matrix composites reinforced with saffil/ceraklwool and saffil/Si particle prepared by squeeze casting have been investigated in room temperature and $250^{circ}C$. Adhesive and scuffing wear phenomena was studied when load was changed to 10~40N and wear velocity was 2.0m/s at room temperature and $250^{circ}C$. Generally, the morphology of tensile fractured surface revealed dimple pattern which implies ductile fracture of the composites. However, cleavage fracture was also observed in case of ADC12 alloy based saffil/Si particle composite. The maximum tensile strength of 320MPa was obtained in ADC12 alloy based composites reinforced by saffil/cerakwool(5:5) preformed fibers. In the results of dry wear test, it was observed that scuffing was occurred at 40N in room temperature and 30N for $250^{circ}C$.