Typical metal oxide thin films having optical and electrical properties are widely used as inorganic functional materials. Liquid phase deposition(LPD) method, a new low temperature process, has been developed for the several advantages of no vacuum system, low cost, high throughput, and low processing temperature(<$50^{circ}C$). Silica powder was added to 40wt% hydrofluoro-silicic acid($H_2$SiFulcorner) to obtain an immersing solution of silica-saturated hydrofluorosilicic acid solution. Boric acid solution was continuously added in the range from 0 to 0.05M to prepare supersaturated hydrofluorosilicic acid solution. LPD $SiL_2$film was formed with the variation of added amount of $H_2$O. The SiO$_2$thin film could be prepared from hydrofluorosilicic acid by LPD method. The thickness of LPD $_SiO2$film was influenced by the boric acid concentration and added amount of $H_2$O. Silicon in thin film existed as SiFulcorner by Raman spectrum.