The corrosion behavior of heat-resistant alloys, More 1 and Super 22H in molten salts of LiCl and $LiCl-Li_2$O was investigated in the temperature range of $650~850^{circ}C$. In a molten salt of LiCl, a dense protective oxide scale of $LiCrO_2$ was formed, following growth of oxide scale with parabolic kinetics. But in a mixed molten salt of LiCl, a dense protective oxide scale of $LiCrO_2$ was formed, following growth of oxide scale with parabolic kinetics. But in a mixed molten salt of $LiCl-Li_2$O, a porous non-protective scale of Liulcorner(Cr, Ni, Fe)ulcornerO$_2$was formed, following growth of oxide scale with linear kinetics. The corrosion rate increased slowly with the increase of temperature up to $750^{circ}C$, but above $750^{circ}C$ rapid increase in corrosion rate observed. The corrosion behavior of Super 22H alloy was similar to that of More 1 alloy, but Super 22H showed higher corrosion resistance than More 1.