The interfacial reaction and joint properties of Sn-3.5Ag/Cu and Sn-3.5Ag-1Zn/Cu joint were studied. Modified double lap shear solder joints of Sn-3.5Ag and Sn-3.5Ag- lZn solder were aged for 60days at $100^{circ}C$ and $150^{circ}C$ and then loaded to failure in shear. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-lZn at the aging temperature of $150^{circ}C$ Through the SEM/EDS analysis of solder joint, it was proved that intermatallic layer was $Cu_{6}Sn_5$ phase and aged specimens showed that intermatallic layer grew in proportion to $t_{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_{6}Sn_{5}$ phase formed at the side of substrate and $Cu_{5}Zn_{8}$ phase formed at the other side in double layer. The shear strength of the Sn-3.5Ag/Cu joint improved by addition of IZn. The strength of the joint increases with strain rate and decreases with aging temperature