The rolling fatigue lives (RFL) of five kinds of silicon nitride balls were investigated. Four kinds of Si$_3$N$_4$balls were fabricated using different raw materials, sintering aids and sintering conditions. Commercially available Si$_3$N$_4$ball was also studied for comparison. All the balls were finished up to the dimensional accuracy of Grade 10 defined in KS B 2001 (Steel Balls fer Ball Bearings) with a size of 9.525 mm. RFL tests were then conducted under the initial theoretical maximum contact stress 6.38 GPa and the spindle speed 10,000 rpm. Gear oil was provided by oiled race as lubricant. The results of RFL test indicated the prerequisitic conditions for the long rolling life of Si$_3$N$_4$ball : (1) the high density, (2) microstructures consisted of small uniformly distributed grains, (3) little glassy phase in grainboundary, and (4) little crystalline phase and secondary phase that induces residual thermal stress due to the differences of thermal expansion coefficient with Si$_3$N$_4$phase.