Tencel fabrics were treated with cellulase after mechanical prefibrillation treatment. SEM analysis was carried out to study morphological change of the treated fabric. The cellulase-treated Tencel fabrics were evaluated for weight loss and tensile strength. X-ray diffraction method, moisture regain, and K/S value were used to elucidate crystalline structural changes occurred by cellulase treatment. Degree of polymerization and copper number of the cellulase-treated fabrics were also measured to estimate effect of hydrolysis. SEM analysis indicated that with treatment of prefibrillation and cellulase, fibrils were produced and damage occurred deep into the fiber. Increases in concentration and time of cellulase treatment increased weight loss and decreased tensile strength retention of the treated fabrics. As cellulase hydrolysis progressed, degree of crystallinity, moisture regain and K/S value were not much changed. (Korean J Human Ecology 2(1) : 142∼148, 1999)