The increase in color depth of polyester fiber dyed with black disperse dyes was investigated with respect to the kinds of resins and alkali treatment. The color depth of the dyed polyester fiber increased continuously according to the concentration of resins coated onto the fabrics. The alkali treatment to polyester fiber before dyeing also enhanced the color depth. It was thought that the polyester fiber was hydrolyzed by alkali resulting micropores on the sample. And the following treatment with a resin, Jet Black T-101, to the polyester fiber increased the color depth much higher. The successive process of alkali treatment, dyeing and Jet Black T-101 treatment could give the best color depth to polyester fiber. Although the alkali treatment reduced the tensile strength of polyester fiber, the color depth of polyester fiber enhanced sufficiently within the range of practically acceptable weight loss and strength. To analyze the micropore on the polyester fiber formed by alkali treatment, nitrogen porosimeter was used. As the weight loss of polyester fiber treated with alkali increased, the BET(Brunauer-Emmett-Teller) surface area, total pore volume, and average pore size of the sample increased.