To develop the manufacturing technique for the powder builder of amorphous solid types, the water glass mixed with caustic soda dispersed into the methanol. Thus soluble sodium silicate was made a form of amorphous solid powder. In order to examine characteristics of water soluble sodium silicate $SiO_2/Na_2O$ mol ratio, we investigated solubility, thermogram, SEM, and BET analysis. pH buffering capacity, calcium-ion binding capacity as temperature change, and surfactant loading capacity were examined for characteristics as laundry detergent builder. $SiO_2/Na_2O$ molar ratio of soluble sodium silicate was 1.0, 2.4, 2.8, and zeolite was used in order to investigate basic characteristics of laundry detergent builder. Silicate used with laundry detergent was good for pH buffering capacity and solubility. But calcium-ion binding capacity and surfactant adsorption ability were lower. $SiO_2/Na_2O$ mol ratio became higher, pH buffering capacity and ion exchange ability were lower and surfactant adsorption ability was a little higher.