A numerical analysis was performed to predict flow curves and dynamic recrystallization behaviors of Al-5wt%Mg alloy on the basis of results of hot compression tests. The hot compression tests were carred out in the ranges of 350 ~ 500 ${^circ}C$ and 5 ${ imes}{10^-3}$ ~ 3 ${ imes}{10^0}$/sec to obtain the Zener-Hollomon parameter Z. The modelling equation for flow stress was a function of strain, strain rate, temperature. The influence of these variables was quantifield using the Zener-Hollomon parameter. In the modelling equation, the effects of strain hardening and dynamic recrystallization were taken into consideration. Therefore, the modelling stress-strain curves of Al-5wt%Mg alloy were in good agreement with experimental results. Finally, the dynamic recrystallization kinetics were illustrated through the inspection of microstructure after deformation.