Carbon nitride coatings on the substrates of 0.55wt% C - 1.68wt% Mn induction-hardened rolling elements were prepared by ion beam assisted deposition. It was found through metallographic observation that the carbon nitride coatings appeared lamellar-type repeated layers parallel to the surface of substrate. Surface roughness of the coated specimens was improved in comparison with that of the substrates. Wear resistance of the coatings was evaluated using Polymet RCF-1 machine with a constant supply of lubricant followed by Weibull statistical analysis and scanning electron microscopy. the results indicated failure due to old-age wear-out of the coatings was mainly caused by numerous micropits formed on the wear track during repeated rolling contact.