Hardness characteristics and microstructures of $Nb/MoSi_2$ laminate composites were evaluated from the variation of fabricating conditions such as preparation temperature, applied pressure and pressure holding time. $Nb/MoSi_2$ laminate composites composed of $MoSi_2$ powder and Nb sheets were fabricated by the hot press. From experimental results, it was found that the lamination from Nb sheet and $MoSi_2$ powder was an excellent strategy to improve hardness characteristics of monolithic $MoSi_2$. However, interfacial reaction products like(Nb, Mo)$SiO_2;and;Nb2Si_3$ formed at the interface of $Nb/MoSi_2$ and increased with fabricating temperature.