This study was performed to evaluate the effect of resin and filler type on the fracture toughness of light-activated composites. Experimental composites were prepared using urethane tetramethacrylate(UTMA) and bisphenol glycidylmethacrylate(Bis-GMA) monomers and five different types of silica fillers. Fracture toughness was measured by a single edge V-notched beam(SEVNB) method, which was discussed from ASTM E399-78. Rectangular bars of $2.5{ imes}5{ imes}26mm$ were prepared with experimental composites and a notch about 2.25mm deep was carved at the center of the long axis of the specimen using a dental diamond disk driven by a dental micro engine. The flexural test was carried out at a crosshead speed of 0.05mm/min and fracture surfaces were observed under scanning electron microscope. The results obtained were summarized as follows: 1. The fracture toughness values of UTMA-based composites were relatively higher than those of Bis-GMA-based composites. 2. The highest fracture toughness value was observed in the UTMA-based composite containing the $1.5{mu}m$-spherical fillers. 3 Aging in the distilled water at $37^{circ}C$ for 10 days showed the increase of fracture toughness, which was severer in the Bis-GMA-based composites than those of UTMA-based composites. 4. The AE amplitude occurring during the fracture toughness tests was the highest at the point of macroscopic fracture.