Penning type sputtering system which has two opposed targets was implemented and the physical characteristics of the deposited carbon nitride films were investigated. When argon ratio was reduced and nitrogen ratio was increased in the sputtering gas mixture, Fe was less sputtered. The grain size of grown carbon nitride films was distributed from $150{AA}$ to $250{AA}$. As nitrogen partial pressure increases, growth rate and nitrogen incorporation in the film increases.