The composite restorative resins have their insufficient resistance to wear. The subsurface degradation within the restoration is considered to be associated with wear. The aim of this study was to evaluate the resistance to degradation of six commercial composite resins in an alkaline solution. The brands studied were Clearfil APX(Kuraray), Heliomolar(Vivadent), Surefil(Dentsply), TPH(Dentsply), Tetric Ceram(Vivadent), and Z100(3M). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{circ}C$. After 14 days they were removed, neutralized with HCL, washed with water and dried to constant mass at $60^{circ}C$. Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights; (b) Si loss (ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The mass loss was in descending order by Z100, TC H, S, CL, TPH and in the range of $0.45sim3.64%$ 2. The degradation layer depth was in descending order by H, Z100, S, TC, TPH, CL and in the range of $10.85sim73.38{mu}m$ 3. For the Si concentration, Z100 was the highest of all 4. The highly significant correlation(r=0.81, p<0.05) was observed between mass loss and degradation depth. 5. Under scanning electronmicroscopy, the degradation of connection between resin matrix and fillers was observed 2 weeks after soaking in NaOH solution.