($Pb_{0.91}$$La_{0.09}$)($Zr_{0.65}$$Ti_{0.35}$)$O_3$ thin films were prepared on ITO-coated glass by spin-coating. As $Pb_{0.9}$$La_{0.1}$)$TiO_3$ thin films were used as seeding layers, formation temperature of perovskite was reduced and theUrosette" structure was disappeared. PLZT thin films with a seeding layer of 40 nm thick showed a (100) preferred orientation and better dielectric and ferroelectric properties.ties.