Kraft Lignin which is produced abundantly in pulp industry, was chemically degraded into small oligomers and polymerized using horseradish peroxidase. Lignin acidolysis was optimized by controlling reaction time and HCI concentration. Acidolyzed lignin was polymerized and copolymers of acidolyzed lignin and phenol or p-cresol were synthesized. 70% of kraft lignin was degraded after acidolysis. Number average molecular weight of all lignin polymers were from 8,500 to 14,000 and did not show large difference. Differential scanning calorimeter analysis showed that acidolyzed lignin did not show any melting temparature under $300^{circ}C$, which indicates that newly synthesized lignin polymers can be used in industry under mild condition.