LiMn2O4 thin fiolm cathodes for Li-ion secondary battery were fabricated by r.f. magnetron sputtering technique. As-deposited films were amorphous. A spinel structure could not be obtained LiMn2O4 films by in-situ thermal annealing. After post thermal annealing over $700^{circ}C$ in oxygen atmosphere, LiMn2O4 films prepared above 100 W r.f. power could be crystallized into a spinel structure. The electrochemical property of the LiMn2O4 film cathodes was tested in a Li/1 M LiClO4 in PC/LiMn2O4 cell. From cyclic voltammetry at scan rate of 2mV/sec of 2.5~4.5V, LiMn2O4 electrode prepared by post annealing at 75$0^{circ}C$ showed good initial capacity. LiMn2O4 electrode prepared by post annealing at 80$0^{circ}C$ showed the best crycling performance.