YAG(Y3Al5O12) as host material of YAG:Tb3+ was studied via hydrothermal synthesis of metal hydroxides. We changed the kind of mineralizer, the concentrations and process conditions in hydrothermal synthesis. As a result, we found, acicular YAG powders were obtained by the use of KOH as a mineralizer, the concentration of KOH affected the shape and size of YAG powder. Fine grained YAG were perpared by the use of NH4OH as a mineralizer and the concentration of NH4OH affected crystal phases but did not affect particle size. We could finally get the spherical looking YAG powder at 8 M NH4OH and at 35$0^{circ}C$ for 12h. The average particle size was about 0.2${mu}{ extrm}{m}$.