Alnite clinker, which is based on CaO-SiO2-CaCl2 system, was synthesized by recycling Cl-containing waste, and its hydraulic properties were onvestigated. Alinite coinkers with two different chemical compositions were burned for 10∼30 minutes in the range of temperature, 1350∼1450$^{circ}C$. The microstructures of those clinkers were characterized by powder X-ray diiffracuion analysis, optical microscope, and scanning electronic microscope and heat of hydration of alinite cements which was measured in order to investigate hydraulic properties. X-ray analysis shwoed that f-CaO in both clinkers with different compositions significantly was decreased with transforming C2S(belite) to C3S(alite). From the results of microscopy and scanning electron microscopy(SEM), crystal of synthesized alite(C3S) was larger and better crystallinity than that of ordinary portland cement.