Samples with the nominal composition, Bi2-xGexSr2CaCu2O8＋$delta$ (x=0, 0.1, 0.2, 0.3, 0.4, 0.5) were prepared by the solid-state reaction method. We have studied the effect of substitution Ge for Bi and investigated the superconducting properties by changing oxygen content with Ge substitution. It was found that temperature difference, ΔK, between TCon and TCzero was considerably smaller in the samples prepared by the intermediate pressing method than that in the samples by the solid-state reaction method. We found the solubility limit of Ge to the 80 K single phase was around x=0.3. Within the solubility limit, lattice constant c decreased with the increase of x. In the region of the 80K single phase, the onset critical temperature TCon increased and excess oxygen content decreased with increase of x.