UV-curable resin has the properties of quick-drying, high productivity at low temperature, energy, space saving, solventless, non-polluting and low-stinking, and thus, UV-curing system has been widely used in the fields of printing inks, adhesives, paints and coating agents. This study has been executed to develop a new functionnal material by the polymerization induced phase separation. The results obtained were as follows. As for the curing properties of the monomer/prepolymer/alkyd resin blends, it was found out that there was a peak by the polymerization induced phase separation when measuring the changes of viscosity and elasticity. It was also found out that such polymerization phase separation occurred in case that the alkyd resin contents were 20wt% and 30wt% and not found at the contents of 40wt%. Therefore, it would be desirable to maintain the contents of alkyd resin at less than 30wt% in order to use the polymerization induced phase separation.