Extraction of manganese was investigated with nitric acid from the dust which was generated in the AOD process producing a medium-low carbon ferromanganese from a high carbon ferromanganese. Content of manganese oxide in the dust was about 90%, and phase of it was confirmed as $Mn_3O_4$, The $Mn_3O_4$ particles was agglomerated as spherical shape, and had a lot of pore and crack inside. Maximum recovery of Mn from the sample in the leaching step was about 67% and residue was the amorphous $MnO_2$. The extraction of Mn increased with increasing temperature, but decreased in proportion to concentration of nitric acid. The extraction rate was in good agreement with the pore diffusion model.