Low density ceramic supporter was prepared by using fly ash as a starting mterial with borax or glass powders. Also the wheat powders were used by 30 wt% to increase the initial porosity of the supporter. The density of the supporter decreased as the amount of borax increased. The bulk density of $0.79g/ extrm{cm}^3$ and the apparent density of $1.10g/ extrm{cm}^3$ were obtained when the fly ash with 15% of borax was sintered at $1160^{circ}C$ for 15 minutes. The density also decreased as the plate glass powders past through $212mu extrm{m}$ size were mixed. When the fly ash with 12% of glass powder was sintered at $1280^{circ}C$ for 10 minutes, the bulk and apparent density were $0.90g/ extrm{cm}^3$ and $1.00g/ extrm{cm}^3$, respectively.