In order to improve organic vapor separation efficiency of polydimethylsiloxane (PDMS) membrane, various zeolites (zeolite 4A, zeolite 13X and natural zeolite) were introduced into a thin PDMS film. The measurements of permeability and selectivity of zeolite-filled PDMS membranes were carried out with a CO$_2$gas and a CO$_2$gas/acetic acid vapor mixture, respectively. The CO$_2$permeability of zeolite-filled membranes decreased with increasing zeolite content and then recovered up to 30 wt% content. The effect of zeolite type on the improvement of CO$_2$permeability was found to be in the order of zeolite 13X > natural zeolite > 4A. The CO$_2$selectivity of zeolite-filled membranes was enhanced up to 9 times compared with the selectivity of a pure (unfilled) PDMS membrane. The effect of zeolite type on the improvement of CO$_2$selectivity was found to be in the order of natural zeolite > zeolite 13X > zeolite 4A.