This study was carried out to investigate the effect of the type of base papers containing rice straw-BKP on the properties and printabilities of coated papers. Also, it was intended to evaluate the effect of coated paper prepared with anionic and amphoteric latex based coating color. The results obtained from this study were as follows. The fiber length of rice straw-BKP was observed much shorter than those of the wood pulps(Sw-BKP, Hw-BKP). This has effect on physical properties. Therefore, the results of measured physical properties were much lower than those of wood pulps. Also, physical properties tended to increase slightly with the increase of the mixing ratio of Sw-BKP. Opacity of the base paper containing rice straw-BKP, was higher than that of the wood pulps. As the mixing ratio of Sw-BKP increases the opacity tended to decrease. On the other hand, smoothness and roughness to rice straw-BKP were similar with Sw-BKP and its air permeability was lower than those of wood pulps. The optical properties of coated papers containing rice straw-BKP tended to be similar to those of other base papers. The ink receptivity of coated papers containg rice straw-BKP was higher than those of wood pulps and printing gloss was similar to wood pulps. The mixing ratio of Sw-BKP, the ink receptivity and printing gloss of rice straw-BKP were showed no difference irrespective the mixing ratio of Sw-BKP. Meannwhile, amphoteric latex improved the optical properties and printability of coated papers.