Bi₁₂SiO₂₀, Bi₁₂GeO₂₀ and Bi₁₂O₂₀ compounds with the sillenite crystal structure were synthesized and sintered into the dense ceramic bodies. An analyses of the microwave dielectric properties of the Si, Ge and Ti sillenites showed a permittivity (e) of ∼40 and a negative temperature coefficient of the resonant frequency for all analogues (from -20 to -40 ppm/K). The Qxf value of the Si and Ge sillenites was measured to be ∼8.000 GHz. The Ti analogue shows a significantly lower Qxf value(∼2.500 GHz) and is sensitive to the heat-treatment conditions. By increasing the sintering temperature the size of the grains increases, which correlates with an increase in the Qxf value.